Plate 5 was removed from service in late 1851 for an unknown reason. Around the first of September 1855 the reliefs on plate 5 were re-entered from the transfer roll, and the plate was placed back in service. This re-entry, or strengthening, resulted in the late state of plate 5 (5L).
The surface of the plate suffered damage in the form of pitting or corrosion, presumably from rust, during the nearly four years it was in storage. This damage is visible in many of the stamps printed from plate 5L in the form of spots of color where there should be none. The first illustration shows four stamps printed from one of the most "rusty" positions (58R5L) of plate 5L. The rust damage is clearly evident as consistent spots of color in the "S" of U.S., and in the surrounding areas, especially in the adjacent periods and in the upper margin. The effects of the rust damage on plate 5L are a great aid to plating those stamps that show the resulting spots.
Position 58R5L also happens to show a distinctive upper frame line that is a
good example of a plating aid. The line, if followed from left to right,
bends down sharply so it comes very close to the upper label block just before
the "S" of U.S. Then it gradually rises until it peaks
approximately over the "T" of POSTAGE, after which it levels out
somewhat. The horizontally-compressed image at left simulates what the
upper frame line would look like if observed at a low angle.